Cracks in Injection Molded Parts and Fixes

Why Do Custom Plastic Injection Products Crack? A Comprehensive Troubleshooting Guide

Plastic injection molding[^1] is a precise art, but defects can still occur. One of the most frustrating issues manufacturers face is cracking in injection-molded parts.

Cracking can manifest as surface crazing (silky cracks), micro-cracks, stress whitening (white marks at stress points), or complete fracture. These defects can happen immediately during demolding or later during the product's application.

In this guide, we break down the root causes of these cracks—ranging from processing errors to mold design flaws[^2]—and provide actionable solutions. > Key Takeaway: Cracking is rarely caused by a single factor. It is usually a combination of residual stress, external force, and material weakness.

1. Processing Factors (Machine Settings)

Improper machine settings are the most common cause of internal stress leading to cracks.

Excessive Pressure & Speed: If the injection pressure is too high, the filling speed is too fast, or the packing time is too long, the part will suffer from excessive internal stress.
Demolding Speed: If the mold opens too quickly or with too much force, it can physically pull and crack the part, especially if it hasn't cooled sufficiently.
온도 제어:
- Mold Temperature: If the mold is too cold, the part may not release easily, leading to stress.
- Material Temperature: If the barrel temperature is too high, the plastic may degrade (burn), reducing its mechanical strength.
Weld Lines: Poor processing can lead to weak weld lines where the plastic flow fronts meet, creating weak points prone to cracking.

솔루션:

사출 압력 및 속도를 줄입니다.
Shorten injection and holding times.
Adjust the mold opening speed to be smoother.
Annealing: Perform heat treatment (annealing) immediately after molding to relieve residual stress.

2. Mold Design Issues

The physical design of the mold dictates how the plastic flows and cools. Flaws here create inherent weak points.

Ejection System: If the ejector pins are unbalanced, too few, or have too small a surface area, the ejection force concentrates on small areas, causing cracks.
Sharp Corners: Sharp corners act as stress concentrators.
Metal Inserts: Using metal inserts can be problematic because metal and plastic shrink at different rates during cooling, creating high internal stress around the insert.
Vacuum Lock: Deep-draw parts need air vents. Without them, a vacuum forms, making the part stick and potentially crack during ejection.

솔루션:

Ensure sufficient draft angles and polished cavity surfaces.
Use fillets (rounded corners) instead of sharp angles to distribute stress.
Minimize the use of metal inserts or design the mold to accommodate shrinkage differences.
Add vents to deep cavities to prevent vacuum formation.

3. Material Selection & Quality

Even with a perfect mold and machine, bad material will result in failure.

Recycled Material: Using too much regrind (recycled plastic) lowers the tensile strength and impact resistance of the part.
Moisture: Many engineering plastics (like Nylon or PC) are hygroscopic. If not dried properly, moisture reacts with the polymer during melting (hydrolysis), causing the material to become brittle and crack.
오염: Mixing different types of plastics or using contaminated raw materials will compromise structural integrity.

4. Machine & Process Factors

Plasticizing Capacity: The injection molding machine must be sized correctly.
- Too Small: The plastic won't mix or melt thoroughly, leading to brittleness.
- Too Large: The plastic stays in the barrel too long and degrades due to heat.
Back Pressure & Screw Speed: Excessive 역압[^3] or screw speed generates shear heat, degrading the material properties.

Summary: Troubleshooting Table

Here is a quick reference guide to help you diagnose the source of the cracking.

카테고리	Potential Cause	Recommended Solution
Processing	High Injection Pressure / Speed	Lower pressure; Reduce injection speed.
Processing	High Residual Stress	Increase mold temp; Anneal part after molding.
금형 설계	Sharp Corners / Bad Geometry	Add radius (fillets) to corners; Avoid sharp transitions.
금형 설계	Ejection Issues	Polish cavity; Increase draft angle; Balance ejector pins.
재료	Moisture / Wet Resin	Dry material properly before processing.
재료	Too much Recycled Content	Reduce regrind ratio; Use virgin material.
Machine	Degradation	Check barrel temperature; Ensure correct screw size.

결론

Cracking in custom plastic injection products is a complex issue that requires a systematic approach to solve. By analyzing the processing parameters, 금형 설계, 및 material quality, you can identify the root cause.

Start by checking your material drying process and reducing injection speeds, as these are the most common culprits. If problems persist, review your mold design for stress concentrators like sharp corners or insufficient draft angles.

Need help with your injection molding project? Contact us today for expert manufacturing solutions.

[^1]: Explore this resource to discover essential best practices that enhance quality and efficiency in plastic injection molding. [^2]: Identifying mold design flaws is crucial for improving product quality. [^3]: Understanding back pressure can help optimize your injection molding process.

저자 소개

Alex Yu

아이디얼 프로 매뉴팩처링

알렉스는 Ideal Pro의 공동 창립자이지만, 주요 프로젝트를 총괄하거나 기술 팀을 이끌지 않을 때는 장거리 자전거 타기를 즐기거나, 동네에서 가장 맛있는 커피를 찾아다니거나, 다음 여행 계획을 세우는 모습을 볼 수 있습니다. 국제 무역 영업과 프로젝트 관리 분야에서 20년 이상의 경력을 쌓아온 그는 촉박한 마감 기한부터 까다로운 엔지니어링 문제까지, 그 사이의 모든 상황을 다 겪어보았습니다. 그는 훌륭한 성과는 충분한 휴식을 취한 마음과 맛있는 커피에서 나온다고 믿으며, 맡은 모든 프로젝트에 그와 같은 호기심과 세심한 주의를 기울입니다. 사무실에 있지 않을 때는 대개 야외 어딘가에서 새로운 장소를 탐험하며, 나중에 나눌 이야기를 수집하곤 합니다.