사출 성형[^1] is a complex dance of temperature, pressure, and time. Among these, injection speed (ram speed)[^2] plays a pivotal role in determining the quality of the final part.

Why is speed segmentation so critical? Because the velocity of the melt front directly affects molecular orientation and internal stress. To achieve a stable melt surface speed and minimize defects, you cannot rely on a single speed setting. You must master speed segmentation.

In this guide, we will explore the golden rules of speed profiling and how to adjust them for different geometries and materials.

> ? Pro Tip: Since melt flow velocity[^3] is difficult to measure directly, we often calculate it indirectly by measuring the screw forward speed or cavity pressure (assuming the non-return valve is leak-free).

The Golden Rules of Speed Segmentation

To ensure a smooth transition from one set point to another and maintain a constant fluid surface speed, we recommend adhering to the following principles:

1. Constant Surface Speed: The velocity of the melt front should ideally remain constant.
2. Prevent Freezing: Use rapid injection to prevent the melt from freezing prematurely during the filling process.
3. Critical Areas: Balance the need for rapid filling in runners with reduced speed at the gate (entry point).
4. Stop Immediately: Ensure the injection stops the moment the cavity is filled to prevent over-packing, flash, and residual stress.
5. Geometry Matters: Settings must account for mold geometry, flow restrictions, and instability factors.

Material & Geometry Considerations

Material characteristics are paramount. Polymers can degrade due to excessive stress. While higher melt temperatures can lead to oxidation, they also reduce viscosity and shear stress.

Speed segmentation is particularly helpful for heat-sensitive materials[^4] such as PC (Polycarbonate), POM (Acetal), and UPVC.

Mold Geometry Guidelines

Troubleshooting Defects via Speed Control

Most injection molding defects can be solved by adjusting the injection speed. Here is how to tackle common issues.

1. Gate Defects (Burn Marks & Flow Lines)

When melt passes through a gate, the surface may cool or stagnate. If the speed is too high, excessive shear creates pressure peaks, leading to gate burns 또는 flow lines.

• The Fix: Decelerate just before the gate to prevent excessive shear, then accelerate once through.
• 참고: Precise control at the gate is difficult; decelerating at the end of the runner is often a more practical solution.

2. Flash & Air Traps (End of Fill)

Over-packing causes flash (excess material escaping the mold), while poor venting causes air traps.

• The Fix: Use a slow speed in the final segment of injection. This prevents over-filling and allows air to escape through vents, reducing residual stress.

3. Short Shots

If the speed is too slow at the gate or if the melt freezes locally, you get a short shot (incomplete part).

• The Fix: Increase injection speed immediately after passing the gate or local flow obstructions.

4. Jetting (Snake-like Streams)

Jetting occurs when the melt shoots through the gate without attaching to the mold walls. This is common with low viscosity materials or high barrel temperatures.

• The Fix: The key is finding the transition point. You must fill the runner quickly, then slow down significantly as you pass through the gate. If you switch too late, inertia causes jetting.

Summary: Speed Adjustments for Common Defects

Use this table as a quick reference for your process optimization.

결론

Smooth parts depend on injection speed. Whether you are working with glass-fiber-filled materials (which are sensitive to shear) or heat-sensitive polymers, the logic remains the same: maintain a stable melt front velocity.

By understanding the relationship between geometry, material viscosity, and injection speed, you can eliminate defects like short shots[^5], flash, and burns. Mastering speed segmentation is not just a setting—it is the art of injection molding.

[^1]: Explore cutting-edge advancements in injection molding to enhance your production efficiency and part quality. [^2]: Understanding injection speed is crucial for optimizing the quality of molded parts. [^3]: Learn about the methods to measure melt flow velocity for better process control. [^4]: Explore the challenges and strategies for working with heat-sensitive materials. [^5]: Learn how to identify and fix short shots for better production outcomes.

저자 소개

Alex Yu

아이디얼 프로 매뉴팩처링

알렉스는 Ideal Pro의 공동 창립자이지만, 주요 프로젝트를 총괄하거나 기술 팀을 이끌지 않을 때는 장거리 자전거 타기를 즐기거나, 동네에서 가장 맛있는 커피를 찾아다니거나, 다음 여행 계획을 세우는 모습을 볼 수 있습니다. 국제 무역 영업과 프로젝트 관리 분야에서 20년 이상의 경력을 쌓아온 그는 촉박한 마감 기한부터 까다로운 엔지니어링 문제까지, 그 사이의 모든 상황을 다 겪어보았습니다. 그는 훌륭한 성과는 충분한 휴식을 취한 마음과 맛있는 커피에서 나온다고 믿으며, 맡은 모든 프로젝트에 그와 같은 호기심과 세심한 주의를 기울입니다. 사무실에 있지 않을 때는 대개 야외 어딘가에서 새로운 장소를 탐험하며, 나중에 나눌 이야기를 수집하곤 합니다.